Material – ASTM A 182 F1925
Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings and Valves and Parts for High-Temperature Service
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM A 182 F1925 Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings and Valves
and Parts for High-Temperature Service
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Pipe Flanges, Forged Fittings and Valve
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.020 max. |
| Silicon | Si % | 0.500 max. |
| Manganese | Mn % | 1.000 max. |
| Chromium | Cr % | 19.000 - 21.000 |
| Sulphur | S % | 0.030 max. |
| Molybdenum | Mo % | 6.000 - 7.000 |
| Phosphorus | P % | 0.045 max. |
| Copper | Cu % | 0.800 - 1.500 |
| Nitrogen | N % | 0.100 - 0.200 |
| Nickel | Ni % | 24.000 - 26.000 |
| Iron | Fe % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 600 min. |
| Yield Strength in Mpa | 295 min. |
| Elongation in % | 30 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B 649 N08925 | ASTM | USA | Bar and Wire |
| B 625 N08925 | ASTM | USA | Plate, Sheet and Strip |
| B 673 N08925 | ASTM | USA | Pipe |
| B 674 N08925 | ASTM | USA | Tube |
| B 677 N08925 | ASTM | USA | Pipe and Tube |
| SB-625 N08925 | ASME | USA | Plate, Sheet and Strip |
| SB-649 N08925 | ASME | USA | Bar and Wire |