Material – ASTM B 166 N06617
Standard Specification for Nickel-Chromium-Iron Alloys and Nickel-Chromium-Cobalt- Molybdenum Alloy Rod, Bar and Wire
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 166 N06617 Nickel-Chromium-Iron Alloys and Nickel-Chromium-Cobalt-Molybdenum Alloy
Rod, Bar and Wire
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Rod, Bar and Wire
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.050 - 0.150 |
| Silicon | Si % | 1.000 max. |
| Manganese | Mn % | 1.000 max. |
| Copper | Cu % | 0.500 max. |
| Sulphur | S % | 0.015 max. |
| Chromium | Cr % | 20.000 - 24.000 |
| Cobalt | Co % | 10.000 - 15.000 |
| Molybdenum | Mo % | 8.000 - 10.000 |
| Iron | Fe % | 3.000 max. |
| Aluminium | Al % | 0.800 - 1.500 |
| Titanium | Ti % | 0.600 max. |
| Boron | B % | 0.006 max. |
| Nickel | Ni % | 44.500 min. |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 655 min. |
| Yield Strength in Mpa | 240 min. |
| Elongation in % | 35 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B 167 N06617 | ASTM | USA | Pipe and Tube |
| B 168 N06617 | ASTM | USA | Plate, Sheet and Strip |
| B 564 N06617 | ASTM | USA | Forging |
| B 626 N06617 | ASTM | USA | Tube |
| B 546 N06617 | ASTM | USA | Pipe |
| - | - | - | - |
| - | - | - | - |