Material – ASTM B 408 N08120
Standard Specification for Nickel-Iron-Chromium Alloy Rod and Bar
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 408 N08120 Nickel-Iron-Chromium Alloy Rod and Bar
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Rod and Bar
| Chemical Composition | Chemical Composition | ||||
|---|---|---|---|---|---|
| Carbon | C % | 0.020 - 0.100 | Nickel | Ni % | 35.000 - 39.000 |
| Silicon | Si % | 1.000 max. | Iron | Fe % | Balance |
| Manganese | Mn % | 1.500 max. | - | - | - |
| Chromium | Cr % | 23.000 - 27.000 | - | - | - |
| Sulphur | S % | 0.030 max. | - | - | - |
| Boron | B % | 0.010 max. | Heat Treatment | ||
| Copper | Cu % | 0.500 max. | As-Cast or Annealing or Age Hardning | ||
| Aluminium | Al % | 0.400 max. | |||
| Titanium | Ti % | 0.200 max. | Mechanical Properties | ||
| Niobium | Nb % | 0.400 - 0.900 | Tensile Strength in Mpa | 621 min. | |
| Molybdenum | Mo % | 2.500 max. | Yield Strength in Mpa | 276 min. | |
| Phosphorus | P % | 0.040 max. | Elongation in % | 30 min. | |
| Tungsten | W % | 2.500 max. | Reduction of Area in % | - | |
| Cobalt | Co % | 3.000 max. | Hardness in BHN | - | |
| Nitrogen | N % | 0.150 - 0.300 | Impact in Joule | - | |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B 163 N08120 | ASTM | USA | Tube |
| B 407 N08120 | ASTM | USA | Pipe and Tube |
| B 409 N08120 | ASTM | USA | Plate, Sheet and Strip |
| B 564 N08120 | ASTM | USA | Forging |
| SB-163 N08120 | ASME | USA | Tube |
| N08120 | UNS | USA | Forging |
| - | - | - | - |