Material – ASTM B 626 N10675
Standard Specification for Nickel and Nickel-Cobalt Alloy Tube
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 626 N10675 Nickel and Nickel-Cobalt Alloy Tube
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Tube
| Chemical Composition | Chemical Composition | ||||
|---|---|---|---|---|---|
| Carbon | C % | 0.010 max. | Tantalum | Ta % | 0.200 max. |
| Silicon | Si % | 0.100 max. | Zirconium | Zr % | 0.100 max. 94.000 - |
| Manganese | Mn % | 3.000 max. | Ni + Mo | Ni% + Mo% 98.000 | |
| Copper | Cu % | 0.200 max. | Nickel | Ni % | 65.000 min. |
| Sulphur | S % | 0.010 max. | - | - | - |
| Chromium | Cr % | 1.000 - 3.000 | Heat Treatment | ||
| Phosphorus | P % | 0.030 max. | As-Cast or Annealing or Age Hardning | ||
| Molybdenum | Mo % | 27.000 - 32.000 | |||
| Iron | Fe % | 1.000 - 3.000 | Mechanical Properties | ||
| Cobalt | Co % | 3.000 max. | Tensile Strength in Mpa | 760 min. | |
| Tungsten | W % | 3.000 max. | Yield Strength in Mpa | 350 min. | |
| Vanadium | V % | 0.200 max. | Elongation in % | 40 min. | |
| Titanium | Ti % | 0.200 max. | Reduction of Area in % | - | |
| Tungsten | W % | 3.000 max. | Hardness in BHN | - | |
| Niobium | Nb % | 0.200 max. | Impact in Joule | - | |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B 333 N10675 | ASTM | USA | Plate, Sheet and Strip |
| B 335 N10675 | ASTM | USA | Rod |
| B 564 N10675 | ASTM | USA | Forging |
| B 472 N10675 | ASTM | USA | Bar |
| B 619 N10675 | ASTM | USA | Pipe |
| B 622 N10675 | ASTM | USA | Pipe and Tube |
| - | - | - | - |