Material – ASTM B 637 N07080
Standard Specification for Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 637 N07080 Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging
Stock for Moderate or High Temperature Service
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Bars, Forgings and Forging
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.100 max. |
| Silicon | Si % | 1.000 max. |
| Manganese | Mn % | 1.000 max. |
| Chromium | Cr % | 18.000 - 21.000 |
| Sulphur | S % | 0.015 max. |
| Aluminium | Al % | 0.500 - 1.800 |
| Iron | Fe % | 3.000 max. |
| Titanium | Ti % | 1.800 - 2.700 |
| Nickel | Ni % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 930 min. |
| Yield Strength in Mpa | 620 min. |
| Elongation in % | 20 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| Nimonic Alloy 80A | Gravity | India | Pipe, Tube, Sheet, Strip, Plate, Hexagon and Wire |
| SB-637 N07080 | ASME | USA | Bars, Forgings and Forging |
| N07080 | UNS | USA | Bars, Forgings and Forging |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |