Material – ASTM B 649 R20033
Standard Specification for Ni-Fe-Cr-Mo-Cu Low-Carbon Alloy, Ni-Fe-Cr-Mo-Cu-N Low- Carbon Alloys and Cr-Ni-Fe-N Low-Carbon Alloy Bar and Wire
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 649 R20033 Ni-Fe-Cr-Mo-Cu Low-Carbon Alloy, Ni-Fe-Cr-Mo-Cu-N Low-Carbon Alloys and Cr-Ni-
Fe-N Low-Carbon Alloy Bar and Wire
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Bar and Wire
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.015 max. |
| Silicon | Si % | 0.500 max. |
| Manganese | Mn % | 2.000 max. |
| Chromium | Cr % | 31.000 - 35.000 |
| Sulphur | S % | 0.010 max. |
| Molybdenum | Mo % | 0.500 - 2.000 |
| Phosphorus | P % | 0.020 max. |
| Nitrogen | N % | 0.350 - 0.600 |
| Copper | Cu % | 0.300 - 1.200 |
| Nickel | Ni % | 30.000 - 33.000 |
| Iron | Fe % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 750 min. |
| Yield Strength in Mpa | 380 min. |
| Elongation in % | 40 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B 564 R20033 | ASTM | USA | Forging |
| B 462 R20033 | ASTM | USA | Pipe Flanges, Forged Fittings and Valve |
| B 619 R20033 | ASTM | USA | Pipe |
| B 622 R20033 | ASTM | USA | Pipe and Tube |
| B 626 R20033 | ASTM | USA | Tube |
| B 625 R20033 | ASTM | USA | Plate, Sheet and Strip |
| SB-649 R20033 | ASME | USA | Bar and Wire |