Material – ASTM B86 Zamak 3
Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloy Foundry and Die Castings
Group - Non-Ferrous Zinc Alloy
Sub Group - ASTM B86 Zinc and Zinc-Aluminum (ZA) Alloy Foundry and Die Castings
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Aluminium | Al % | 3.700 - 4.300 |
| Cadmium | Cd % | 0.004 max. |
| Chromium | Cr % | 0.020 max. |
| Copper | Cu % | 0.100 max. |
| Iron | Fe % | 0.050 max. |
| Magnesium | Mg % | 0.020 - 0.060 |
| Manganese | Mn % | 0.060 max. |
| Nickel | Ni % | 0.020 max. |
| Lead | Pb % | 0.005 max. |
| Silicon | Si % | 0.035 max. |
| Tin | Sn % | 0.002 max. |
| Titanium | Ti % | 0.001 max. |
| Zinc | Zn % | Balance |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Aging |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 283 min. |
| Yield Strength in Mpa | 221 min. |
| Elongation in % | 10 min. |
| Reduction of Area in % | - |
| Hardness in HB | 82 min. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| Zamak 3 | ANSI/AA | USA | Casting |
| ZP3 | ISO | International | Casting |
| Z33521 | UNS | USA | Ingot and Casting |
| B86 Alloy 3 | ASTM | USA | Casting |
| B86 AG40A | ASTM | USA | Casting |
| ZnAl4 | UNI | Italy | Ingot and Casting |
| B240 Zamak 3 | ASTM | USA | Casting |