Material – ASTM B271 Nickel Alumium Bronze UNS C95500
Standard Specification for Copper-Base Alloy Centrifugal Castings
Group - Non-Ferrous Copper Alloy
Sub Group - ASTM B271 Copper-Base Alloy Centrifugal Castings
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Rod, Bar, Tube and Shapes
| Chemical Composition | ||
|---|---|---|
| Iron | Fe % | 3.000 - 5.500 |
| Ni + Co | Ni% + Co% 3.000 - 5.500 | - |
| Aluminium | Al % | 10.000 - 11.500 |
| Manganese | Mn % | 3.500 max. |
| Copper | Cu % | 78.000 min. |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Solution Annealing or Annealing or Normalizing |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 620 min. |
| Yield Strength in Mpa | 275 min. |
| Elongation in % | 6 min. |
| Reduction of Area in % | - |
| Hardness in BHN | 190 min. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B148 C95500 | ASTM | USA | Casting |
| B30 C95500 | ASTM | USA | Ingot and Casting |
| B271 C95500 | ASTM | USA | Casting |
| SB-148 C95500 | ASME | USA | Casting |
| SB-505 C95500 | ASME | USA | Casting |
| CA955 | SAE | USA | Casting |
| C95500 | SAE | USA | Casting |