Material ‐ ASTM B584 C94800
Standard Specification for Copper Alloy Sand Casting for General Applications
Group - Non ‐ Ferrous Copper Alloy
Sub Group - ASTM B584 Copper Alloy Sand Casting for General Applications
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | Heat Treatment | |||
|---|---|---|---|---|
| Aluminium | Al % | 0.005 max. | ||
| Iron | Fe % | 0.250 max. | ||
| Manganese | Mn % | 0.200 max. | ||
| Ni + Co | Ni% + Co% 4.500 ‐ 6.000 | As ‐ Cast | ||
| Phosphorus | P % | 0.050 max. | ||
| Lead | Pb % | 0.300 ‐ 1.000 | ||
| Sulphur | S % | 0.050 max. | ||
| Antimony | Sb % | 0.150 max. | ||
| Silicon | Si % | 0.005 max. | Mechanical Properties | |
| Tin | Sn % | 4.500 ‐ 6.000 | Tensile Strength in Mpa | 276 min. |
| Zinc | Zn % | 1.000 ‐ 2.500 | Yield Strength in Mpa | 138 min. |
| Copper | Cu % | 84.000 ‐ 89.000 | Elongation in % | 20 min. |
| ‐ | ‐ | ‐ | Reduction of Area in % | ‐ |
| ‐ | ‐ | ‐ | Hardness in BHN | ‐ |
| ‐ | ‐ | ‐ | Impact in Joule | ‐ |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| C94800 | UNS | USA | Rod, Bar, Tube and Shapes |
| B292 ‐ B | ASTM | USA | Casting |
| B30 C94800 | ASTM | USA | Ingot and Casting |
| B505 C94800 | ASTM | USA | Casting |
| SB ‐ 505 C94800 | ASME | USA | Casting |
| C94800 | SAE | USA | Casting |
| CA948 | SAE | USA | Casting |