Material – ASTM F562 R30035
Standard Specification for Cobalt-35 Nickel-20 Chromium-10 Molybdenum Alloy for Surgical Implant Applications
Group - Non-Ferrous Cobalt Alloys
Sub Group - ASTM F562 R30035 Cobalt-35 Nickel-20 Chromium-10 Molybdenum Alloy for Surgical Implant
Applications
Application - Intended for Valve, Pump, General Engineering, Automotive, Medical and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.025 max. |
| Chromium | Cr % | 19.000 - 21.000 |
| Molybdenum | Mo % | 9.000 - 10.500 |
| Nickel | Ni % | 33.000 - 37.000 |
| Iron | Fe % | 1.000 max. |
| Silicon | Si % | 0.150 max. |
| Manganese | Mn % | 0.150 max. |
| Phosphorus | P % | 0.015 max. |
| Sulphur | S % | 0.010 max. |
| Titanium | Ti % | 1.000 max. |
| Boron | B % | 0.015 max. |
| Cobalt | Co % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 793 - 2482 |
| Yield Strength in Mpa | 241 - 586 |
| Elongation in % | 1.800 min. |
| Reduction of Area in % | 35 min. |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| F 2527 R30035 | ASTM | USA | Casting |
| R30035 | UNS | USA | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |