Material – BS 3100 Grade 332C11
Standard Specification for Steel Castings for General Engineering Purposes
Group - Ferrous Stainless Steel Alloys
Sub Group - BS 3100 Grade 332C11 Steel Castings for General Engineering Purposes
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.070 max. |
| Silicon | Si % | 1.500 max. |
| Manganese | Mn % | 1.500 max. |
| Phosphorus | P % | 0.040 max. |
| Sulphur | S % | 0.040 max. |
| Chromium | Cr % | 19.000 - 22.000 |
| Molybdenum | Mo % | 2.000 - 3.000 |
| Nickel | Ni % | 27.500 - 30.500 |
| Copper | Cu % | 3.000 - 4.000 |
| Iron | Fe % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As Cast or Annealing or Normalizing or Hardening and Tempering |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 425 min. |
| Yield Strength in Mpa | 170 min. |
| Elongation in % | 34 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| Z 2 NCDU 25.20.04 M | AFNOR NF | France | Casting |
| 2074/H9A | AS | Australia | Casting |
| A 351 Grade CN7M | ASTM | USA | Casting |
| A 743 Grade CN-7M | ASTM | USA | Casting |
| A 743 N08007 | ASTM | USA | Casting |
| A 744 Grade CN-7M | ASTM | USA | Casting |
| SA-351 Grade CN7M | ASME | USA | Casting |