Material – BS 3100 Grade 425C12
Standard Specification for Steel Castings for General Engineering Purposes
Group - Ferrous Stainless Steel Alloys
Sub Group - BS 3100 Grade 425C12 Steel Castings for General Engineering Purposes
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.060 max. |
| Silicon | Si % | 1.000 max. |
| Manganese | Mn % | 1.000 max. |
| Phosphorus | P % | 0.040 max. |
| Sulphur | S % | 0.030 max. |
| Chromium | Cr % | 11.500 - 14.000 |
| Nickel | Ni % | 3.500 - 4.500 |
| Molybdenum | Mo % | 0.400 - 1.000 |
| Iron | Fe % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As Cast or Annealing or Normalizing or Hardening and Tempering |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 755 min. |
| Yield Strength in Mpa | 550 min. |
| Elongation in % | 15 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 2074/H3D | AS | Australia | Casting |
| 3444 Grade 24 | IS | India | Casting |
| A 352 Grade CA6NM | ASTM | USA | Casting |
| 4899 Grade 10 | IS | India | Casting |
| A 352 J91540 | ASTM | USA | Casting |
| SA-352 Grade CA6NM | ASME | USA | Casting |
| SCS 6 | JIS | Japan | Casting |