Material ‐ BS 10213 EN 1.4317
Standard Specification for Steel Castings for Pressure Purposes
Group - Ferrous Stainless Steel Alloys
Sub Group - BS 10213 Steel Castings for Pressure Purposes
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.060 max. |
| Silicon | Si % | 1.000 max. |
| Manganese | Mn % | 1.000 max. |
| Phosphorus | P % | 0.035 max. |
| Sulphur | S % | 0.025 max. |
| Chromium | Cr % | 12.000 ‐ 13.500 |
| Nickel | Ni % | 3.500 ‐ 5.000 |
| Molybdenum | Mo % | 0.700 max. |
| Copper | Cu % | 0.300 max. |
| Vanadium | V % | 0.080 max. |
| Iron | Fe % | Balance |
| ‐ | ‐ | ‐ |
| ‐ | ‐ | ‐ |
| ‐ | ‐ | ‐ |
| ‐ | ‐ | ‐ |
| Heat Treatment |
|---|
| Normalising or Annealing or Hardening + Tempering |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 760 ‐ 960 |
| Yield Strength in Mpa | 550 min. |
| Elongation in % | 15 min. |
| Reduction of Area in % | ‐ |
| Hardness in BHN | ‐ |
| Impact in Joule | 27 min. @ ‐ 120 ̊ C |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 1.6982 | BS | British | Casting |
| 1.6982 | DIN | Germany | Casting |
| GX3CrNi13 ‐ 4 | UNI | Italy | Casting |
| GX3CrNi13 ‐ 4 | DIN | Germany | Casting |
| GX3CrNi13 ‐ 4 | EN | European Union | Casting |
| GX3CrNi13 ‐ 4 | AFNOR NF | France | Casting |
| X2CrNiMo13 ‐ 4 | DIN | Germany | Forging |