Material – BS EN-GJS-350-22-LT
Standard Specification For Spheoidal Graphiite Cast Irons Castings
Group - Ferrous SG Iron I Ductile Iron Alloys
Sub Group - BS EN-GJS-350-22-LT Spheoidal Graphiite Cast Irons Castings
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | - |
| Silicon | Si % | - |
| Manganese | Mn % | - |
| Phosphorus | P % | - |
| Sulphur | S % | - |
| Chromium | Cr % | - |
| Nickel | Ni % | - |
| Copper | Cu % | - |
| Iron | Fe % | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 310 min. |
| Yield Strength in Mpa | 200 min. |
| Elongation in % | 12 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 350-22-LT | ISO | International | Casting |
| JS 350-22-LT | AS | Australia | Casting |
| EN-GJS-350-22-LT | UNE | Spain | Casting |
| EN-JS1015 | BS | British | Casting |
| 5.3100 | EN | European Union | Casting |
| EN-JS1015 | UNI | Italy | Casting |
| EN-GJS-350-22-LT | DIN | Germany | Casting |