Material – DIN 2.4175
Standard Specification for Nickel and Nickel-Copper Alloy Casting
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN 2.4175 Nickel and Nickel-Copper Alloy Casting
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 1.000 - 2.500 |
| Silicon | Si % | 2.000 max. |
| Manganese | Mn % | 1.500 max. |
| Copper | Cu % | 1.200 max. |
| Iron | Fe % | 1.000 max. |
| Other | Ot% | 0.200 max. |
| Ni + Co | Ni% + Co% | 93.000 min. |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 340 min. |
| Yield Strength in Mpa | 160 min. |
| Elongation in % | 10 min. |
| Reduction of Area in % | - |
| Hardness in HRB | 85 min. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| G-Ni93C | DIN | Germany | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |