Material – DIN 2.4654
Standard Specification for Nickel and Nickel Alloy Casting
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN 2.4654 Nickel and Nickel Alloy Casting
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.020 - 0.100 |
| Silicon | Si % | 0.150 max. |
| Manganese | Mn % | 1.000 max. |
| Chromium | Cr % | 18.000 - 21.000 |
| Aluminium | Al % | 1.200 - 1.600 |
| Boron | B % | 0.003 - 0.010 |
| Cobalt | Co % | 12.000 - 15.000 |
| Copper | Cu % | 0.100 max. |
| Iron | Fe % | 2.000 max. |
| Molybdenum | Mo % | 3.500 - 5.000 |
| Phosphorus | P % | 0.015 max. |
| Sulphur | S % | 0.015 max. |
| Titanium | Ti % | 2.800 - 3.300 |
| Zirconium | Zr % | 0.020 - 0.080 |
| Nickel | Ni % | Balance |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 1100 min. |
| Yield Strength in Mpa | 760 min. |
| Elongation in % | 15 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| NiCr20Co13Mo4Ti3Al | DIN | International | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |