Material – DIN NiCr16 Fe 7 TiAl
Standard Specification for Nickel and Nickel Alloy Casting
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN NiCr16 Fe 7 TiAl Nickel and Nickel Alloy Casting
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.080 max. |
| Silicon | Si % | 0.500 max. |
| Manganese | Mn % | 1.000 max. |
| Chromium | Cr % | 14.000 - 17.000 |
| Copper | Cu % | 0.500 max. |
| Aluminium | Al % | 0.800 - 1.600 |
| Iron | Fe % | 5.000 - 9.000 |
| Niobium | Nb % | 0.700 - 1.200 |
| Phosphorus | P % | 0.015 max. |
| Sulphur | S % | 0.010 max. |
| Titanium | Ti % | 2.000 - 2.600 |
| Nickel | Ni % | 70.000 min. |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 782 min. |
| Yield Strength in Mpa | 391 min. |
| Elongation in % | 42 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 2.4694 | DIN | Germany | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |