Material – EN 1.1137
Standard Specification for Non-Alloy Steel Rod for Drawing and/or Cold Rolling
Group - Ferrous Mild Steel Alloys
Sub Group - EN 1.1137 Non-Alloy Steel Rod for Drawing and/or Cold Rolling
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Cold Rolling and Rod
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.180 - 0.230 |
| Silicon | Si % | 0.300 max. |
| Manganese | Mn % | 0.300 - 0.500 |
| Phosphorus | P % | 0.020 max. |
| Sulphur | S % | 0.025 max. |
| Chromium | Cr % | 0.100 max. |
| Nickel | Ni % | 0.100 max. |
| Molybdenum | Mo % | 0.050 max. |
| Aluminium | Al % | 0.010 max. |
| Copper | Cu % | 0.150 max. |
| Cu+Ni+Cu | Cu %+Ni %+Cu % 0.300 max. | Yield Strength in Mpa |
| Nitrogen | N % | 0.007 max. |
| Cu+Sn | Cu %+Sn % | 0.150 max. |
| Iron | Fe % | Balance |
| - | - | - |
| Heat Treatment |
|---|
| Annealing or Normalising or Hardening + Tempering |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 414 min. |
| 276 min. | - |
| Elongation in % | 24 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| J02002 | UNS | USA | Casting |
| 1.0414 | DIN | Germany | Cold Rolling and Rod |
| 1020 | AISI | USA | Forging, Bar, Wire, and Shape |
| A216 WCB | ASTM | USA | Casting |
| 1.0619 | DIN | Germany | Casting |
| A352 LCA | ASTM | USA | Casting |
| A732 1A | ASTM | USA | Casting |