Material – ASTM B 462 N06200
Standard Specification for Forged or Rolled Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 462 N06200 Forged or Rolled Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for
Corrosive High-Temperature Service
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Pipe Flanges, Forged Fittings and Valve
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.010 max. |
| Silicon | Si % | 0.080 max. |
| Manganese | Mn % | 0.500 max. |
| Copper | Cu % | 0.300 - 1.900 |
| Sulphur | S % | 0.010 max. |
| Chromium | Cr % | 22.000 - 24.000 |
| Phosphorus | P % | 0.025 max. |
| Molybdenum | Mo % | 15.000 - 17.000 |
| Cobalt | Co % | 2.000 max. |
| Iron | Fe % | 3.000 max. |
| Aluminium | Al % | 0.500 max. |
| Nickel | Ni % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 690 min. |
| Yield Strength in Mpa | 310 min. |
| Elongation in % | 45 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B 564 N06200 | ASTM | USA | Forging |
| B 574 N06200 | ASTM | USA | Rod |
| B 575 N06200 | ASTM | USA | Plate, Sheet and Strip |
| B 619 N06200 | ASTM | USA | Pipe |
| B 622 N06200 | ASTM | USA | Pipe and Tube |
| B 626 N06200 | ASTM | USA | Tube |
| B 472 N06200 | ASTM | USA | Billets and Bars |