Material – ASTM B 564 N06219
Standard Specification for Nickel Alloy Forgings
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 564 N06219 Nickel Alloy Forgings
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Forging
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.050 max. |
| Silicon | Si % | 0.700 - 1.100 |
| Manganese | Mn % | 0.500 max. |
| Chromium | Cr % | 18.000 - 22.000 |
| Sulphur | S % | 0.010 max. |
| Molybdenum | Mo % | 7.000 - 9.000 |
| Phosphorus | P % | 0.020 max. |
| Cobalt | Co % | 1.000 max. |
| Copper | Cu % | 0.500 max. |
| Aluminium | Al % | 0.500 max. |
| Iron | Fe % | 2.000 - 4.000 |
| Titanium | Ti % | 0.500 max. |
| Nickel | Ni % | Balance |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 660 min. |
| Yield Strength in Mpa | 270 min. |
| Elongation in % | 50 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B 446 N06219 | ASTM | USA | Rod and Bar |
| B 443 N06219 | ASTM | USA | Plate, Sheet and Strip |
| B 444 N06219 | ASTM | USA | Pipe and Tube |
| B 704 N06219 | ASTM | USA | Tube |
| B 705 N06219 | ASTM | USA | Pipe |
| SB-443 N06219 | ASME | USA | Plate, Sheet and Strip |
| SB-444 N06219 | ASME | USA | Pipe and Tube |