Material – ASTM B 564 N08367
Standard Specification for Nickel Alloy Forgings
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 564 N08367 Nickel Alloy Forgings
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Forging
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.030 max. |
| Silicon | Si % | 1.000 max. |
| Manganese | Mn % | 2.000 max. |
| Chromium | Cr % | 20.000 - 22.000 |
| Sulphur | S % | 0.030 max. |
| Molybdenum | Mo % | 6.000 - 7.000 |
| Phosphorus | P % | 0.040 max. |
| Nitrogen | N % | 0.180 - 0.250 |
| Copper | Cu % | 0.750 max. |
| Nickel | Ni % | 23.500 - 25.500 |
| Iron | Fe % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 655 min. |
| Yield Strength in Mpa | 310 min. |
| Elongation in % | 30 min. |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B 688 N08367 | ASTM | USA | Plate, Sheet and Strip |
| B 691 N08367 | ASTM | USA | Rod, Bar and Wire |
| B 462 N08367 | ASTM | USA | Pipe Flanges, Forged Fittings, and Valve |
| A 314 N08367 | ASTM | USA | Bar and Forging |
| B 472 N08367 | ASTM | USA | Billet and Bar |
| B 690 N08367 | ASTM | USA | Pipe and Tube |
| B 834 N08367 | ASTM | USA | Pipe Flanges, Forged Fittings, and Valve |