Material – ASTM B 805 N09777
Standard Specification for Precipitation Hardening Nickel Alloys Bar and Wire
Group - Non-Ferrous Nickel Alloys
Sub Group - ASTM B 805 N09777 Precipitation Hardening Nickel Alloys Bar and Wire
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Bar and Wire
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.030 max. |
| Silicon | Si % | 0.500 max. |
| Manganese | Mn % | 1.000 max. |
| Chromium | Cr % | 14.000 - 19.000 |
| Sulphur | S % | 0.010 max. |
| Molybdenum | Mo % | 2.500 - 5.500 |
| Phosphorus | P % | 0.030 max. |
| Niobium | Nb % | 0.100 max. |
| Titanium | Ti % | 2.000 - 3.000 |
| Aluminium | Al % | 0.350 max. |
| Nickel | Ni % | 34.000 - 42.000 |
| Iron | Fe % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 517 min. |
| Yield Strength in Mpa | 207 min. |
| Elongation in % | 25 min. |
| Reduction of Area in % | 35 min. |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| UNS N09777 | UNS | USA | Bar and Wire |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |