Material – ASTM B100 C65500
Standard Specification for Wrought Copper-Alloy Bearing and Expansion Plates and Sheets for Bridge and Other Structural Use
Group - Non-Ferrous Copper Alloy
Sub Group - ASTM B100 Wrought Copper-Alloy Bearing and Expansion Plates and Sheets for Bridge and Other
Structural Use
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Plate and Sheet
| Chemical Composition | ||
|---|---|---|
| Iron | Fe % | 0.800 max. |
| Manganese | Mn % | 0.500 - 1.300 |
| Ni + Co | Ni% + Co% | 0.600 max. |
| Lead | Pb % | 0.050 max. |
| Silicon | Si % | 2.800 - 3.800 |
| Zinc | Zn % | 1.500 max. |
| Cu + Ag | Cu% + Ag% | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| Normalizing or Annealing or Tempering |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 415 min. |
| Yield Strength in Mpa | 170 min. |
| Elongation in % | 10 min. |
| Reduction of Area in % | - |
| Hardness in HRB | 75 min. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B124 C65500 | ASTM | USA | Rod, Bar and Shapes |
| C65500 | AS | Australia | Ingot and Casting |
| B283 C65500 | ASTM | USA | Forging |
| B96 C65500 | ASTM | USA | Plate, Sheet, Strip and Bar |
| B98 C65500 | ASTM | USA | Rod, Bar and Shape |
| SB-98 C65500 | ASME | USA | Rod, Bar and Shape |
| SB-283 C65500 | ASME | USA | Forging |