Material – ASTM B148 Aluminum Bronze UNS C95410
Standard Specification for Alumium - Bronze Sand Castings
Group - Non-Ferrous Alumium Alloy
Sub Group - ASTM B148 Alumium - Bronze Sand Castings
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Ni + Cu | Ni% + Cu% 1.500 - 2.500 | - |
| Manganese | Mn % | 0.500 max. |
| Iron | Fe % | 3.000 - 5.000 |
| Aluminium | Al % | 10.000 - 11.500 |
| Copper | Cu % | 83.000 min. |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Solution Annealing or Normalizing |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 515 min. |
| Yield Strength in Mpa | 205 min. |
| Elongation in % | 12 min. |
| Reduction of Area in % | - |
| Hardness in BHN | 150 min. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| B176 C95410 | ASTM | USA | Casting |
| B271 C95410 | ASTM | USA | Casting |
| B30 C95410 | ASTM | USA | Ingot and Casting |
| B505 C95410 | ASTM | USA | Casting |
| SB-148 C95410 | ASME | USA | Casting |
| SB-505 C95410 | ASME | USA | Casting |
| CACIn702 | KS | Korea | Ingot and Casting |