Material – ASTM B951 AZ80A
Standard Specification for Codification of Unalloyed Magnesium and Magnesium-Alloys
Group - Non-Ferrous Magnesium Alloy
Sub Group - ASTM B951 Codification of Unalloyed Magnesium and Magnesium-Alloys
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Bar and Wire
| Chemical Composition | ||
|---|---|---|
| Aluminium | Al % | 7.800 - 9.200 |
| Copper | Cu % | 0.050 max. |
| Iron | Fe % | 0.005 max. |
| Manganese | Mn % | 0.120 - 0.500 |
| Nickel | Ni % | 0.005 max. |
| Other | Ot% | 0.300 max. |
| Silicon | Si % | 0.100 max. |
| Zinc | Zn % | 0.200 - 0.800 |
| Magnesium | Mg % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Solution Treated or Fully Treated |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 290 - 330 |
| Yield Strength in Mpa | 185 - 230 |
| Elongation in % | 2 - 9 |
| Reduction of Area in % | - |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| Mg-Al8Zn | ISO | International | Bar and Wire |
| MBD-AZ80 | JIS | Japan | Bar and Wire |
| MS-AZ80 | JIS | Japan | Shape |
| MWD-AZ80 | JIS | Japan | Bar and Wire |
| B107 AZ80A | ASTM | USA | Bar, Rod, Tube and Wire |
| MB3 | KS | Korea | Bar |
| MgAl8Zn | DIN | Germany | Bar and Wire |