Material – DIN 1729-1 MgAl8Zn
Standard Specification for Wrought Magnesium Alloys
Group - Non-Ferrous Magnesium Alloy
Sub Group - DIN 1729-1 Wrought Magnesium Alloys
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Bar and Wire
| Chemical Composition | ||
|---|---|---|
| Aluminium | Al % | 7.800 - 9.200 |
| Copper | Cu % | 0.050 max. |
| Iron | Fe % | 0.005 max. |
| Manganese | Mn % | 0.120 - 0.300 |
| Other | Ot% | 0.300 max. |
| Silicon | Si % | 0.100 max. |
| Zinc | Zn % | 0.200 - 0.800 |
| Magnesium | Mg % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Solution Treated or Fully Treated |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 270 - 310 |
| Yield Strength in Mpa | 195 - 215 |
| Elongation in % | 6 - 10 |
| Reduction of Area in % | - |
| Hardness in HB | 60 - 65 |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| Mg-Al8Zn | ISO | International | Bar and Wire |
| MBD-AZ80 | JIS | Japan | Bar and Wire |
| MS-AZ80 | JIS | Japan | Shape |
| MWD-AZ80 | JIS | Japan | Bar and Wire |
| B107 AZ80A | ASTM | USA | Bar, Rod, Tube and Wire |
| B951 AZ80A | ASTM | USA | Bar and Wire |
| MB3 | KS | Korea | Bar |