Material – DIN 2.4368
Standard Specification for Nickel and Nickel-Copper Alloy Casting
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN 2.4368 Nickel and Nickel-Copper Alloy Casting
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.250 max. |
| Silicon | Si % | 3.500 - 4.500 |
| Manganese | Mn % | 0.500 - 1.500 |
| Copper | Cu % | 27.000 - 31.000 |
| Iron | Fe % | 1.000 - 2.500 |
| Aluminium | Al % | 0.500 max. |
| Magnesium | Mg % | 0.120 max. |
| sulphur | S % | 0.010 max. |
| Phosphorus | P % | 0.010 max. |
| Titanium | Ti % | 0.200 max. |
| Other | Ot% | 1.000 max. |
| Ni + Co | Ni% + Co% 61.000 - 68.000 | Elongation in % |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 750 min. |
| Yield Strength in Mpa | 500 min. |
| 1 min. | - |
| Reduction of Area in % | - |
| Hardness in HB | 260 min. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| G-NiCu30Si4 | DIN | Germany | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |