Material – DIN 2.4815
Standard Specification for Nickel and Nickel Alloy Casting
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN 2.4815 Nickel and Nickel Alloy Casting
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.350 - 0.650 |
| Silicon | Si % | 1.000 - 2.500 |
| Manganese | Mn % | 2.000 max. |
| Chromium | Cr % | 12.000 - 18.000 |
| Molybdenum | Mo % | 1.000 max. |
| Phosphorus | P % | 0.040 max. |
| Sulphur | S % | 0.030 max. |
| Nickel | Ni % | 58.000 - 66.000 |
| Iron | Fe % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 400 min. |
| Yield Strength in Mpa | 160 min. |
| Elongation in % | 3 min. |
| Reduction of Area in % | - |
| Hardness in HB | 195 max. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 2.4817 | DIN | Germany | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |