Material – DIN 2.4817
Standard Specification for Nickel and Nickel Alloy Casting
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN 2.4817 Nickel and Nickel Alloy Casting
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.025 max. |
| Silicon | Si % | 0.500 max. |
| Manganese | Mn % | 1.000 max. |
| Chromium | Cr % | 14.000 - 17.000 |
| Copper | Cu % | 0.500 max. |
| Cobalt | Co % | 1.500 max. |
| Aluminium | Al % | 0.300 max. |
| Boron | B % | 0.006 max. |
| Iron | Fe % | 6.000 - 10.000 |
| Phosphorus | P % | 0.020 max. |
| Sulphur | S % | 0.015 max. |
| Titanium | Ti % | 0.300 max. |
| Nickel | Ni % | 72.000 min. |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 500 min. |
| Yield Strength in Mpa | 160 min. |
| Elongation in % | 20 min. |
| Reduction of Area in % | - |
| Hardness in HB | 240 max. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 2.4815 | DIN | Germany | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |