Material – DIN EN 1982 CC750S
Standard Specification for Copper and Copper Alloys - Ingots and Castings
Group - Non-Ferrous Copper Alloy
Sub Group - EN 1982 Copper and Copper Alloys - Ingots and Castings
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Ingot and Casting
| Chemical Composition | ||
|---|---|---|
| Nickel | Ni % | 1.000 max. |
| Lead | Pb % | 1.000 - 3.000 |
| Tin | Sn % | 1.500 max. |
| Aluminium | Al % | 0.100 max. |
| Iron | Fe % | 0.800 max. |
| Manganese | Mn % | 0.200 max. |
| Phosphorus | P % | 0.050 max. |
| Silicon | Si % | 0.050 max. |
| Cu + Ni | Cu%+Ni% 63.000 - 67.000 | Mechanical Properties |
| Zinc | Zn % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 180 min. |
| Yield Strength in Mpa | 70 min. |
| Elongation in % | 12 min. |
| Reduction of Area in % | - |
| Hardness in HB | 45 - 50 |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| CB750S | BS | British | Ingot and Casting |
| CC750S | EN | European Union | Ingot and Casting |
| CC750S | UNI | Italy | Ingot and Casting |
| CC750S | BS | British | Ingot and Casting |
| CACIn202 | KS | Korea | Ingot and Casting |
| CuZn33Pb2-C | PN | Poland | Ingot and Casting |
| CuZn33Pb2-C | AFNOR NF | France | Ingot and Casting |