Material – DIN H-Ni99,95
Standard Specification for Refined Nickel Alloy Castings
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN H-Ni99,95 Refined Nickel Alloy Castings
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | Chemical Composition | ||||
|---|---|---|---|---|---|
| Carbon | C % | 0.015 max. | Zinc | Zn % | 0.002 max. |
| Phosphorus | P % | 0.002 max. | Ni + Co | Ni% + Co% 99.950 min. | |
| Cobalt | Co % | 0.100 max. | - | - | - |
| Copper | Cu % | 0.005 max. | - | - | - |
| Iron | Fe % | 0.020 max. | - | - | - |
| sulphur | S % | 0.0025 max. | Heat Treatment | ||
| Silver | Ag % | 0.0005 max. | As-Cast or Annealing or Age Hardning | ||
| Arsenic | As % | 0.001 max. | |||
| Bismuth | Bi % | 0.0005 max. | Mechanical Properties | ||
| Lead | Pb % | 0.001 max. | Tensile Strength in Mpa | - | |
| Antimony | Sb % | 0.001 max. | Yield Strength in Mpa | - | |
| Selenium | Se % | 0.001 max. | Elongation in % | - | |
| Tin | Sn % | 0.0005 max. | Reduction of Area in % | - | |
| Tellurium | Te % | 0.0005 max. | Hardness in BHN | - | |
| Titanium | Ti % | 0.0005 max. | Impact in Joule | - | |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 2.4017 | DIN | Germany | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |