Material – DIN NiCr25FeAlYC
Standard Specification for Nickel and Chromium Alloy Casting
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN NiCr25FeAlYC Nickel and Chromium Alloy Casting
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.200 - 0.400 |
| Silicon | Si % | 0.500 max. |
| Manganese | Mn % | 0.100 max. |
| Chromium | Cr % | 24.000 - 26.000 |
| Aluminium | Al % | 2.400 - 3.000 |
| Copper | Cu % | 0.150 max. |
| Iron | Fe % | 8.000 - 11.000 |
| Phosphorus | P % | 0.020 max. |
| Sulphur | S % | 0.015 max. |
| Titanium | Ti % | 0.100 - 0.250 |
| Yttrium | Y % | 0.050 - 0.150 |
| Zirconium | Zr % | 0.010 - 0.100 |
| Nickel | Ni % | Balance |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| As-Cast or Annealing or Age Hardning |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 680 min. |
| Yield Strength in Mpa | 270 min. |
| Elongation in % | 30 min. |
| Reduction of Area in % | - |
| Hardness in HB | 220 max. |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 2.4647 | DIN | Germany | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |