Material – DIN NiMo29Cr
Standard Specification for Nickel and Nickel-Iron Alloy Casting
Group - Non-Ferrous Nickel Alloys
Sub Group - DIN NiMo29Cr Nickel and Nickel-Iron Alloy Casting
Application - Intended for Valve, Pump, General Engineering, Automotive and other Industries
Grade Belongs to the Industry - Casting
| Chemical Composition | Chemical Composition | ||||
|---|---|---|---|---|---|
| Carbon | C % | 0.010 max. | Nickel | Ni % | 65.000 min. |
| Silicon | Si % | 0.100 max. | - | - | - |
| Manganese | Mn % | 3.000 max. | - | - | - |
| Iron | Fe % | 1.000 - 6.000 | - | - | - |
| Molybdenum | Mo % | 26.000 - 32.000 | - | - | - |
| Aluminium | Al % | 0.100 - 0.500 | Heat Treatment | ||
| Cobalt | Co % | 3.000 max. | As-Cast or Annealing or Age Hardning | ||
| Chromium | Cr % | 0.500 - 3.000 | |||
| Copper | Cu % | 0.500 max. | Mechanical Properties | ||
| Phosphorus | P % | 0.025 max. | Tensile Strength in Mpa | 750 min. | |
| Sulphur | S % | 0.015 max. | Yield Strength in Mpa | 340 min. | |
| Titanium | Ti % | 0.200 max. | Elongation in % | 35 min. | |
| Vanadium | V % | 0.200 max. | Reduction of Area in % | - | |
| Tungsten | W % | 3.000 max. | Hardness in BHN | 250 max. | |
| Nb + Ta | Nb% + Ta% | 0.400 max. | Impact in Joule | - | |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| 2.4600 | DIN | Germany | Casting |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |
| - | - | - | - |