Material – EN 1.5408
Standard Specification for Steel Rod, Bars and Wire for Cold Heading and Cold Extrusion
Group - Ferrous Mild Steel Alloys
Sub Group - EN 1.5408 Steel Rod, Bars and Wire for Cold Heading and Cold Extrusion
Application - Intended for Valve, Pump, General Engineering, Automotive and Other Industries
Grade Belongs to the Industry - Rod, Bars, Wire and Extrusion
| Chemical Composition | ||
|---|---|---|
| Carbon | C % | 0.280 - 0.320 |
| Silicon | Si % | 0.300 max. |
| Manganese | Mn % | 0.800 - 1.000 |
| Phosphorus | P % | 0.025 max. |
| Sulphur | S % | 0.025 max. |
| Chromium | Cr % | 0.300 max. |
| Boron | B % | 0.0008 - 0.0050 |
| Molybdenum | Mo % | 0.080 - 0.120 |
| Copper | Cu % | 0.250 max. |
| Iron | Fe % | Balance |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| - | - | - |
| Heat Treatment |
|---|
| Annealing or Normalising or Hardening + Tempering |
| Mechanical Properties | |
|---|---|
| Tensile Strength in Mpa | 630 min. |
| Yield Strength in Mpa | - |
| Elongation in % | - |
| Reduction of Area in % | 57 min. |
| Hardness in BHN | - |
| Impact in Joule | - |
Cross Reference Table
| Material | Standard | Country | Grade Belong to the Industry |
|---|---|---|---|
| J03011 | UNS | USA | Casting |
| 1.1811 | DIN | Germany | Casting |
| 161-480 | BS | British | Casting |
| 1030 | AISI | USA | Forging, Bar, Wire, and Shape |
| SCPL1 | JIS | Japan | Casting |
| A732 2Q | ASTM | USA | Casting |
| A732 2A | ASTM | USA | Casting |